2011 aluminum alloy

Zhenhan supplies 2011 aluminum bar, supports bulk purchase, and can be customized according to customer needs.

Fields marked with * must be filled in. Please fill in your commonly used email address or WhatsApp phone number for us to contact you. We value privacy and will not disclose any of your information to any third party.

Product Details

2011Aluminum Alloy Chemical Composition
Cu	Si	Fe	Mn	Mg	Zn	Cr	Pb	Bi	Al
5.0-6.0	≤0.4	≤0.7	≤0.05	≤0.05	≤0.3	≤0.05	0.2-0.6	0.2-0.6	Remainder
2011Aluminum Rod Mechanical Properties
Werkstoff-zustand	Rm/MPa			Rp0,2/MPa			A50 mm /% /min.			HBW/Typischer Wert
T3	≥280			≥210			≥8%			≥90
T4	≥275			≥125			≥16%			≥95
T451	≥275			≥125			≥16%			/
T6	≥295			≥195			≥6%			≥110
T8	≥370			≥270			≥6%			≥115
2011Aluminum Tube Mechanical Properties
Werkstoff-zustand	Rm/MPa			Rp0,2/MPa			A50 mm/% /min.			HBW/Typischer Wert
T3	≥290			≥240			≥6%			≥90
T6	≥310			≥230			≥4%			≥110
T8	≥370			≥275			≥6%			≥115
Aluminium and aluminium alloys – Chemical compositionand form of wrought productsPart 3: Chemical compositionEnglish version of DIN EN 573-3
Aluminium and aluminium alloys-Cold drawn rod/bar and tube Part 2 Mechanical properties:DIN EN 754-2-2008
Aluminium and aluminium alloys-Extruded rod/bar,tube and profiles Part 2:Mechanical properties:DIN EN_755-2-2008
Aluminium and aluminium alloyextruded rods/bars, round bars Chemical composition+Mechanical properties：ASTM B211M-2001
Aluminium and aluminium alloy extruded rods/bars,tubes and profles Chemicalcomposition+Mechanical properties：ASTM B221
Wrought Aluminium and aluminium alloyextruded profles Chemical composition+Mechanical properties:JIS H4100-2006
Wrought Aluminium and aluminium alloy extruded rods/bars Chemical composition+Mechanical properties:JIS H4040-2006
Aluminium and aluminium alloy extruded rods/bars Chemical composition：GB/T3190-2008
Aluminium and aluminium alloy extruded rods/bars Mechanical properties：GB/T3191-2010
2011Applications of Aluminum Materials
This alloy grade offers excellent machinability, high strength, and high hardness, along with a certain degree of heat resistance. Applications include rivets, general mechanical parts, aircraft and missile structures, and other structural components requiring high strength.