7 series aluminum tube

Brand: 7075, 7003, 7050, 7005, 7001, 7049
Characteristics: Good plasticity after solution treatment, particularly good heat treatment strengthening effect, high strength below 150°C, and particularly good low-temperature strength; poor welding performance; tendency to stress corrosion cracking; requires aluminum cladding or other protective treatment before use, etc.

Application: Used in the manufacture of aircraft structures and other high-stress structural parts that require high strength and corrosion resistance, such as aircraft upper and lower wing panels, trusses, bulkheads, trusses, rods, and containers for transportation vehicles; large heat exchangers, and parts that cannot be solid-solution treated after welding; can also be used to manufacture sports equipment such as tennis rackets and softball bats, etc.

Special services: 0 yuan for samples, 0 yuan for door-to-door delivery, and customized services with drawings and samples

Service features: 10,000+ square meters of high-end alloy production base, original factory warranty, 2-15 days delivery, nationwide sales

Fields marked with * must be filled in. Please fill in your commonly used email address or WhatsApp phone number for us to contact you. We value privacy and will not disclose any of your information to any third party.

Product Details

Aluminum Chemical Composition
Grades	Cu	Si	Fe	Mn	Mg	Zn	Cr	Ti	Pb+Bi	Al
7003	≤0.2	≤0.3	≤0.35	≤0.3	0.5-1.0	5.0-6.5	≤0.2	≤0.2	/	Remainder
7005	≤0.1	≤0.35	≤0.4	0.2-0.7	1.0-1.8	4.0-5.0	0.06-0.2	0.01-0.06	0.08-0.2	Remainder
7075	1.2-2.0	≤0.4	≤0.5	≤0.3	2.1-2.9	5.1-6.1	0.18-0.28	≤0.2	/	Remainder
7475	≤0.1	≤0.55	≤0.5	≤0.1	≤0.1	≤0.1	≤0.05	≤0.05	≤0.05	Remainder
Aluminum Bar Mechanical Properties
Grades	RmMPa		Rp0,2MPa			A50 mm% min.			HBW Typischer Wert
7003	≥340		≥280			≥8%			≥110
7005	≥340		≥270			≥8%			≥110
7075	≥540		≥480			≥5%			≥150
7475	≥552		≥496			≥12%			≥150
Aluminum Tube Mechanical Properties
Grades	RmMPa		Rp0,2MPa			A50 mm% min.			HBW Typischer Wert
7003	≥340		≥280			≥8%			≥110
7005	≥340		≥290			≥8%			≥110
7075	≥540		≥485			≥4%			≥150
7475	≥552		≥496			≥12%			≥150
Spot Regular Status
O、H111、T5、T6、T6510、T6511、T73、T73541、T73511
Spot Routine Implementation Standards
Aluminium and aluminium alloys – Chemical compositionand form of wrought productsPart 3: Chemical compositionEnglish version of DIN EN 573-3
Aluminium and aluminium alloys-Cold drawn rod/bar and tube Part 2 Mechanical properties:DIN EN 754-2-2008
Aluminium and aluminium alloys-Extruded rod/bar,tube and profiles Part 2:Mechanical properties:DIN EN_755-2-2008
Aluminium and aluminium alloyextruded rods/bars, round bars Chemical composition+Mechanical properties：ASTM B211M-2001
Aluminium and aluminium alloy extruded rods/bars,tubes and profles Chemicalcomposition+Mechanical properties：ASTM B221
Wrought Aluminium and aluminium alloyextruded profles Chemical composition+Mechanical properties:JIS H4100-2006
Wrought Aluminium and aluminium alloy extruded rods/bars Chemical composition+Mechanical properties:JIS H4040-2006
Aluminium and aluminium alloy extruded rods/bars Chemical composition：GB/T3190-2008
Aluminium and aluminium alloy extruded rods/bars Mechanical properties：GB/T3191-2010